Antiferromagnetic Ordering of Gd^(3+) in Gd2CuO4-δ and (Gd1.85Ge0.15)CuO4-δ

G. H. Hwang；J. H. Shieh；H. C. Ku；J. C. Ho

Chinese Journal of Physics

30卷3期（1992 / 06 / 01）

351 - 355

英文

Calorimetric studies were made between 2 and 18 Kon twoT.-214 compounds, Gd2CuO4-δ and (Gd1.85Ce0.15)CuO4-δ.Antiferromagnetic orderingof Gd^(3+) prevails in both cases, each with a λ-like heat capacity anomaly at TN = 6.6 K and 5.3 K, respectively. A broad shoulder in heat capacity follows with a peak near 2 K. By integrating the area under experimental data and an appropriate extrapolation to zero temperature in a C/T versus T plot, the magnetic entropy associated with the ordering is indeed close to 2Rln8 or 1.85Rln8 per mole of compound, corresponding to the expected value for Gd^(3+) with J = S = 7/2.

1. 張凱婷(2016)。獨立董事與管理階層之社會性連結對董事監督及諮詢角色之影響。淡江大學會計學系碩士班學位論文。2016。1-53。 
2. 呂國精(2017)。具側鏈苯胺五聚體之電活性聚醯胺在金屬防腐蝕上之應用研究。中原大學化學系學位論文。2017。1-103。 
3. 劉力瑋(2017)。發展具有比例螢光輸出酸性應答型前藥奈米粒子應用於藥物制放。國立臺灣大學化學系學位論文。2017。1-132。 
4. 劉曉橋(2017)。氟與氰基取代的有機小分子材料之合成、性質與太陽能電池應用。國立臺灣大學化學系學位論文。2017。1-147。 
5. 姜翰昕(2011)。運用第一原理計算及分子動態模擬探討鋰矽合金之液相與非晶相之基本結構與性質。國立臺灣大學材料科學與工程學系學位論文。2011。1-99。 
6. 戴志杰(2016)。快速脈衝光照在正向偏壓下對非晶矽氧化銦鎵鋅薄膜電晶體汲極電流響應之研究。交通大學光電工程系所學位論文。2016。1-57。