鋼筋混凝土樑鋼板貼片補強後再受溫之性能研究

The Performance of Steel Plate Reinforced RC Beam Subjected to High Temperature

10.6377/JA.200803.0115

周逢霖(Feng-Lin Chou)；郭詩毅(Shih-Yi Kuo)；涂耀賢(Yaw-Shen Tu)；林慶元(Ching-Yuan Lin)

鋼板補強樑 ； 高溫 ； 撓度 ； Steel Plate Reinforced RC Beam ； High Temperature ； Deflection

建築學報

63期（2008 / 03 / 28）

115 - 129

繁體中文

本文研究之目的是藉由試驗探討鋼筋混凝土樑鋼板貼片補強後遭受高溫之行為表現。本文選用鋼板補強樑為研究標的，試體共四支，一支為不補強不受溫之原型試體、一支為補強不受溫試體、兩支為補強試體各受最高溫為150℃及200℃。樑斷面採用建築中常用之尺寸，補強則採用鋼板貼覆於樑底以補強彎矩強度之作法。試體完成後先進行預載，隨後在維持預載中進行升溫試驗，當達到預定溫度後將試體冷卻至室溫，最後進行試體壓壞試驗。試驗進行中量測試體內外側溫度變化、最大撓度變化以及極限強度等數據。由試驗結果發現：補強試體之強度隨受溫之增高而降低，另補強試體在預載加熱階段中之最大撓度與跨度比遠大於未受溫補強試體，且補強試體受溫後之破壞最大撓度與跨度比明顯較未受溫之補強試體大。

The purpose of this research is to study the behaviors of steel plate reinforced RC beam subjected to high temperature through tests. There were four RC beams tested in this research. The first one was without reinforcement and was not heated. The second one was reinforced but not subjected to high temperature. The third and fourth one were reinforced and heated up to 150℃ and 200℃ respectively. The reinforced specimen was strengthened by a steel plate bonded to the specimen's bottom. After curing, the specimen was pre-stressed and then heated with increasing temperature. After heating, all the specimens were left to cool down to the room temperature and then loaded to failure. It is found from the test results that the ultimate strength of reinforced specimen is decreased with increasing temperature and the maximum deflection of heated reinforced specimen is far larger than the non-heated reinforced one during both heating and loading to failure stages.

1. 黃世建、鍾立來、簡文郁、葉勇凱、周德光、葉永信、邱建國、王翊光(2005)。中小學校舍耐震評估與補強工作之芻議。建築學報，54，75-90。
   連結：
2. Abrams, M. S.(1973).Temperature and Concrete.ACI publication SP25.
3. American Society for Testing and Materials(1980).ASTM standards in building codes.Philadelphia, Pa.
4. El-Mihilmy, Mahmoud T.,Tedesco, Joseph W.(2000).Analysis of Reinforced Concrete Beams Strengthened with FRP Laminates.Journal of Structural Engineering,126(6),684-691.
5. Lee, A.,Lichtenhan, J. D.(1999).Thermal and Viscoelastic Property of Epoxy-Clay and Hybrid Inorganic-Organic Epoxy Nanocomposites.Journal of Applied Polymer Science,173,1993-2001.
6. Lin, T. D.,Zwiers, R. I.,Shirley, S. T.,Burg, R.G.(1988).Pullout Tests of Epoxy Coated Bars at High Temperatures.ACI Materials Journal,544-550.
7. Swamy, R. N.,Jones, R.,Bloxham, J.W.(1987).Structural Behavior of Reinforced Concrete Beams Strengthened by Epoxy-Bonded Steel Plates.The Structural Engineer,65(2),59-68.
8. 中國土木水利工程學會(2000)。混凝土工程設計規範與解說（土木401-86a）第二版。中國土木水利工程學會混凝土工程委員會研究報告，14
9. 內政部建築研究所(1999)。921集集大地震建築物震害調查初步報告。台北:內政部建築研究所。
10. 內政部營建署(1998)。建築技術規則。台北:內政部。
11. 王仲宇(1995)。鋼筋混凝土結構物維修補強技術講習會論文集。台北:
12. 何明錦、吳傳威、彭添富(1998)。內政部建築研究所專題研究計劃成果報告MOIS 872011內政部建築研究所專題研究計劃成果報告MOIS 872011,台北:。
13. 吳卓夫(1997)。鋼筋混凝土之損壞與修補。新進混凝土技術對未來土木工程的影響研討會論文集，台北:
14. 高金盛、陳舜田(1996)。火害後鋼筋混凝土樑強度與勁度之衰減。中國土木水利工程學刊，8(3)，371-386。
15. 高健章、鄭啓龍(1997)。混凝土與補強鋼板間膠結界面受溫度之影響。結構工程，12(4)，101-109。
16. 郭詩毅、林慶元(2005)。鋼板貼片補強用環氧樹脂受溫後黏結性質變化研究。中國土木水利工程學刊，17(1)，1-10。
17. 郭詩毅、許銘顯、涂耀賢、黃進興(1995)。RC樑彎矩補強應用鋼板貼片法之設計分析。第十七屆第一次建築研討會論文集，台北:
18. 經濟部中央標準局(2002)。中國國家標準CNS 12514：建築物構造部分耐火試驗法。台北:經濟部中央標準局。
19. 熊光華(1999)。內政部建築研究所專案研究計畫成果報告No. MOIS 881007內政部建築研究所專案研究計畫成果報告No. MOIS 881007,台北:。
20. 蕭興台、宋永鑾、廖肇昌(1994)。RC構件鋼板補強工法之探討。結構工程，9(4)，79-96。