台灣二葉松木材－塑膠複合材之理學機械性質

Physicomechanical Properties of Wood-Plastic Composites Made from Pinus taiwanensis

10.29898/SHBQ.200912.0006

張懋如(Mao-Ju Chang)；吳東霖(Tung-Lin Wu)；洪克昌(Ke-Chang Hung)；陳載永(Tsai-Yung Chen)；吳志鴻(Jyh-Horng Wu)

台灣二葉松 ； 木材塑膠複合材 ； 抽出成分 ； 理學機械性質 ； 界面性質 ； Pinus taiwanensis ； Wood-plastic composites ； Extractive ； Physicomechanical properties ； Interfacial properties

林業研究季刊

31卷4期（2009 / 12 / 01）

65 - 74

繁體中文

本研究係探討台灣本土樹種台灣二葉松應用於木材塑膠複合材(Wood-plastic composites, WPC)時，其粒片尺寸、添加量及抽出成分對複合材理學及機械性質之影響。試驗結果顯示，以木材粒片尺寸6-16 mesh及添加量爲60%所製備之WPC，爲兼具木質材料利用與機械性質之最適配比，而隨著木材粒片尺寸的減小及添加量的增加，其機械性質則有下降之現象。此外，當木材粒片／HDPE混合比(wt%)由20/80增加到80/20時，其抗彎彈性模數有先增後降的情形。另一方面，以醇苯萃取後之木材粒片所製備的WPC，其吸水厚度膨脹率雖較未萃取者高，但抗彎強度及木螺釘保持力則具有較佳表現，顯示台灣二葉松抽出成分會影響木材粒片與塑膠之界面性質，進而導致抗彎強度及木螺釘保持力呈現下降的現象。

This study investigated the effect of wood particle size, wood particle content and extractive on physicomechanical properties of wood-plastic composites (WPC) made from Pinus taiwanensis, a native free in Taiwan. Results demonstrated that the mechanical properties decreased with decreasing wood particle sizes or increasing wood particle contents. With the MOE, the modulus increased as the amount of wood particle increased up to 30% and then leveled off or remained constant up to 60%. Once the wood particle loading exceeded 60%, a significant decrease in the modulus was observed. Accordingly, for mechanical and economic considerations, the WPC with 60 wt% of wood particles (6-16 mesh) should be a suitable formulation. On the other hand, the thickness swelling of the WPC made from extracted wood particle was higher than that made from unextracted one, but the MOR and wood screw-holding strength of resulting WPC made from extracted wood particle were stronger than the other one. These results indicate that extractives of P. taiwanensis might have a negative effect on the interfacial properties between wood particles and polymeric matrix, and resulted in a significant decrease in MOR and wood screw-holding strength of WPC.