High Temperature Superconductors from a Pure Glassy Phase

B. K. Chaudhuri

Chinese Journal of Physics

38卷2S期（2000 / 04 / 01）

211 - 224

英文

Homogenous (Bi3Pb)Sr3Ca3(Cu4¡ nMn)Ox type glassy precursors (M = Li, K, Cr, Mn, Zn, Ti, Ag; and n = 0-0.5) show high Tc superconducting behavior when they are annealed at 840℃ for 24 hrs in air. The superconducting behavior of a typical Cr doped sample is only discussed in this paper. Samples doped with other atoms also behave similarly. All these glasses contain nanocrystalline particles or clusters which grows into the superconducting or other phases by annealing. Single phase high Tc superconductors are obtained from the glasses having nanocrystals size ＜ 20 nm. The suppression of transition temperature supports the pairbreaking mechanism of Abrikosov and Gor'kov. Depending on the measuring temperature, both positive and negative values of the Seebeck coefficients (S) are exhibited by the annealed superconducting samples. Interestingly, small positive peaks were shown by the thermoelectric power (TEP) data of all the doped samples just above Tc. This peak was considered to be associated with the phonon-drag effect. Similar behavior is also exhibited by the correspondingsuperconductors doped with Mn, Fe and Ti. The linear part of the temperature vs. TEP data (above Tc) can be well fitted with the two band model.

1. 李丞斌(2016)。應用賽局觀點探討以網路為基礎服務之策略性合作。淡江大學企業管理學系碩士班學位論文。2016。1-97。 
2. 陳宣蓁(2017)。運用綠色廣告訴求推動綠色產品購買意願-以綠色生活型態為區隔變數。中原大學國際經營與貿易學系學位論文。2017。1-107。 
3. 林怡禎(2016)。掌性金金屬催化重氮化合物與亞硝基苯之環化反應和氧化鎢前驅物合成並應用於原子層沉積薄膜之成長。清華大學化學系所學位論文。2016。1-0。